High Carbon steels Ucingo oluqinileyo ER70S-2 weld fabrication izincedisi
Ifanelekile ukuwelda kombhobho, isitya soxinzelelo, imboni yepetrochemical njalo njalo.
Ziziphi iimpawu?
●Ngenxa yokongezwa kwe-AI, i-Ti, i-Zr kunye nezinye izinto zetsimbi, zingasetyenziselwa ukuthunga i-rust kunye nokungcola phezu kwentsimbi; Ukutya okugudileyo kocingo, i-arc ezinzileyo, ukubunjwa okuhle, ukuhamba kakuhle kwentsimbi etyhidiweyo, ukuchaphaza okuncinci, kunye nenkqubo ye-welding egqwesileyo; Isinyithi esinyibilikisiweyo sineepropati ezizinzileyo zoomatshini kunye nefuthe elihle eliphantsi lobushushu obuphantsi
IParameter yeMveliso
INXENYE YECHEMICAL:
| I-ALLOY(wt%) | C | Si | Mn | P | S | Ni | Cr | Mo | Okunye |
| GB/T IMIGAQO | 0.053 | 0.51 | 1.08 | 0.01 | 0.003 | 0.01 | 0.04 | 0.06 | Ti:0.10 Al:0.07 Zr:0.06 |
IPROPATI YOOMATSHINI:
| IPROPATI | IZIVUNO ZAMANDLA (MPa) | UKWANDISA AMANDLA (MPa) | UBUSHUSHU℃xh | IXABISO LE-IMAPACT J/℃ | Unyango lobushushu °C*h | ||||
| GB/T IMIGAQO | 475 | 550 | 32 | 80/-30 | AW | ||||
IZIQINISEKISO ZOKUSHISA IZIQULATHO:
| INGCACISO YEDIAMETERS(mm) | 1 | 1.2 | 1.6 | |||||
| UMBANE (Amp) | H/W | 80-250 | 100-350 | 250-300 | ||||
| O/W | 70-120 | 80-150 | ||||||
Indlela yothutho
●Uthutho lweemoto
●Ukuhambisa ngenqanawe
Indawo yethu yokugcina impahla
Sithatha inxaxheba kucwangciso
●Ukusetyenziswa kwamandla obushushu
●Itanki yoGcino lwaseShanghai Morimatsu
Iimveliso zethu kwihlabathi
INXENYE YECHEMICAL:
| I-ALLOY(wt%) | C | Si | Mn | P | S | Ni | Cr | Mo | Okunye |
| GB/T IMIGAQO | 0.053 | 0.51 | 1.08 | 0.01 | 0.003 | 0.01 | 0.04 | 0.06 | Ti:0.10 Al:0.07 Zr:0.06 |
IPROPATI YOOMATSHINI:
| IPROPATI | IZIVUNO ZAMANDLA (MPa) | UKWANDISA AMANDLA (MPa) | UBUSHUSHU℃xh | IXABISO LE-IMAPACT J/℃ | Unyango lobushushu °C*h | ||||
| GB/T IMIGAQO | 475 | 550 | 32 | 80/-30 | AW | ||||
IZIQINISEKISO ZOKUSHISA IZIQULATHO:
| INGCACISO YEDIAMETERS(mm) | 1 | 1.2 | 1.6 | |||||
| UMBANE (Amp) | H/W | 80-250 | 100-350 | 250-300 | ||||
| O/W | 70-120 | 80-150 | ||||||